產品參數
| 性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | |
| 基本性能 | 吸水率 | 24小時浸漬(23℃) | ASTM D-570 | 0.7 | % |
| 吸水率 | 飽和(23℃) | ASTM D-570 | 5.4 | % | |
| 物理性能 | 比重 | ASTM D-792 | 1.38 | ||
| 機械性能 | 洛氏硬度M | DAM | ASTM D-785 | M101 | |
| 拉伸強度 | 23℃,DAM | ASTM D-638 | 196.1 | MPa | |
| 埃佐沖擊強度 | 23℃,50%RH | ASTM D-256 | 133 | j/m | |
| 埃佐沖擊強度 | 23℃,DAM | ASTM D-256 | 107 | j/m | |
| 斷裂伸長率 | 23℃,DAM | ASTM D-638 | 3 | % | |
| 撓曲模量 | 23℃,50%RH | ASTM D-790 | 6205 | MPa | |
| 擠剪強度 | 23℃,DAM | ASTM D-732 | 86 | MPa | |
| 撓曲模量 | 23℃,DAM | ASTM D-790 | 8963 | ||
| 撓曲強度 | 23℃,DAM | ASTM D-790 | 262 | MPa | |
| 拉伸強度 | 23℃,50%RH | ASTM D-638 | 124.1 | MPa | |
| 泰伯磨耗量 | 50%RH | 14 | cycles | ||
| 斷裂伸長率 | 23℃,50%RH | ASTM D-638 | 4 | % | |
| 電氣性能 | 介電強度 | DAM | ASTM D-149 | 530 | volts/mil |
| 介電強度 | (分步法) | ASTM D-149 | 440 | volts/mil | |
| 體積電阻率 | 100%RH | ASTM D-257 | 109 | ohm-cm | |
| 體積電阻率 | DAM | ASTM D-257 | 1015 | ohm-cm | |
| 介電常數 | DAM@103Hz赫 | ASTM D-150 | 4.5 | ||
| 介電常數 | 100%RH@106Hz赫 | ASTM D-150 | 10.7 | ||
| 損耗因數 | DAM@103Hz赫 | ASTM D-150 | 0.02 | ||
| 介電常數 | 100%RH@103Hz赫 | ASTM D-150 | 25.0 | ||
| 損耗因數 | 100%RH@106Hz赫 | ASTM D-150 | 0.02 | ||
| 介電常數 | DAM@106Hz赫 | ASTM D-150 | 3.7 | ||
| 熱性能 | 熱畸變溫度 | 1.8MPa | ASTM D-648 | 249 | ℃ |
| 線性熱膨脹系數 | ASTM D-696 | 2.3×10-5 | m/m/℃ | ||
| 熔點 | DAM | ASTM D-789 | 255 | ℃ | |
| 熔點 | 50%RH | ASTM D-789 | 255 | ℃ | |
PA66(聚酰胺66或尼龍66)，同PA6相比，PA66更廣泛應用于汽車工業、儀器殼體以及其它需要有抗沖擊性和高強度要求的產品。
聚酰胺樹脂，英文名稱為polyamide，簡稱PA。俗稱尼龍(Nylon)，它是大分子主鏈重復單元中含有酰胺基團的高聚物的總稱。為五大工程塑料中產量最大、品種最多、用途最廣的品種。尼龍中的主要品種是尼龍6和尼龍66，占絕對主導地位，尼龍6為聚己內酰胺，而尼龍66為聚己二酸己二胺，尼龍66比尼龍6要硬l2%;其次是尼龍11，尼龍12，尼龍610，尼龍612，另外還有尼龍1010、尼龍46、尼龍7、尼龍9、尼龍13，新品種有尼龍6I、尼龍9T和特殊尼龍MXD6(阻隔性樹脂)等，尼龍的改性品種數量繁多，如增強尼龍、單體澆鑄尼龍(MC尼龍)、反應注射成型(RIM)尼龍、芳香族尼龍、透明尼龍、高抗沖(超韌)尼龍、電鍍尼龍、導電尼龍、阻燃尼龍，尼龍與其他聚合物共混物和合金等，滿足不同特殊要求，廣泛用作金屬，木材等傳統材料代用品。